ORP THERMOBOND 65

METATAGS:ORP THERMOBOND 65, ORP TERMOBOND 65, ORP Thermobond 65, orp thermobond 65 , orp termobond 65, Orp Thermobond 65, Orp Termobond 65,
Thermobond 65, THERMOBOND 65 ,TERMOBOND 65, thermobond 65, termobond 65, VA / VeoVa / Acrylic Terpolymer, VA/ VEOVA/ ACRYLIC TERPOLYMER,
VA/ VEOVA/ AKRİLİK TERPOLİMER, va/ veova / acrylic terpolymer, va/ veova/ akrilik terpolimer,Wacker-Vinnapas 5044 N,Wacker-Vinnapas 5043 N,Elotex-FX 2320,Elotex-FX 4300, DOW-DLP 212,DOW-DLP 220,Dairen-DA 1420,Dairen-DA 1450, Momentive-Axilat PAV 30,FAR-Neolith P 6000,Vinavil-5603 P,Wacker-Vinnapas 5044 N,Wacker-Vinnapas 5043 N,Elotex-FX 2320,Elotex-FX 4300, DOW-DLP 212,DOW-DLP 220,Dairen-DA 1420,Dairen-DA 1450, Momentive-Axilat PAV 30,FAR-Neolith P 6000,Vinavil-5603 P



 

 

 

ORP Thermobond 65, koruyucu koloit olarak PVOH ile Vinyl Acetate / VeoVa / Akrilik terpolimer
emülsiyonunun kurutulmasıyla üretilen yeniden dağılabilir bir tozdur. Polimerin spesifik
kimyasal bileşimi, yeniden dağılmış polimerin düşük sıcaklıklarda birleşmesine izin verir ve
mineral substratlar üzerinde iyi yapışma sağlar.
ORP Thermobond 65 hidrolik bağlayıcı içeren karışımları değiştirmek için kullanılır.
ORP Thermobond 65, belirli kimyasal / fiziksel kompozisyonundan dolayı, çimento, alçı
veya kireç gibi hidrolik bağlayıcı içeren harçların yapışma, esneklik ve su direncini artırır.
Özellikle esnek doğasından ötürü ORP Thermobond 65 çapraz deformasyon koşullarında çok iyi
performans gösterir.

ORP THERMOBOND UYGULAMA ALANLARI 65
ORP Thermobond 65, harç formülasyonlarında iyi bir esneklik / elastikiyet, iyileşme ve
Tiksotropik davranış gereklidir.

EIFS (Dış İzolasyon ve Son İşlem Sistemleri) Sıvalar:
Mükemmel esnekliği ve su direnci nedeniyle, ORP Thermobond 65,
EIFS'de EPS ve XPS levhalarına uygulanan çimentolu temel katların imalatı. Önerilen
Dozaj:% 3.0 - 5.0

EIFS'de EPS ve XPS panolar için Yapıştırıcılar:
Önerilen dozlar: 1.0 - 2.0%

Fayans Yapıştırıcıları (S1 & S2):
Önerilen dozlar: 3.0 - 7.0%

ORP THERMOBOND 65 ÜRÜNÜ KULLANIMI - DEPOLAMA - RAF ÖMRÜ
Ambalaj: Her biri 25 kg (450 kg) veya büyük poşet (500 kg) olmak üzere 18 kağıt torba ile palet.
Paketler kuru ve serin bir depoda 10 - 25 ° C arasındaki sıcaklıklarda depolanmalıdır.
Polimerin termoplastik özelliği nedeniyle kekleşmeyi önlemek için paletler birbirinin üstüne
istiflenmemelidir. Neme ve kekleşmeye karşı korunmak için ambalajın kullanımdan sonra iyi kapatılması
gerekir. 6 ay içinde kullanılmalıdır.

 

 

 


ORP Thermobond 65 is a redispersible powder produced by drying an emulsion of Vinyl Acetate /
VeoVa / Acrylic terpolymer with PVOH as protective colloid. The specific chemical composition of the
polymer allows coalescence of the redispersed polymer at low temperatures and provides good
adhesion on mineral substrates.
ORP Thermobond 65 is used to modify mixtures containing hydraulic binders. Due to its particular
chemical / physical composition, ORP Thermobond 65 improves adhesion, flexibility and water
resistance of mortars containing hydraulic binders such as cement, gypsum or lime. Especially because
of the flexible nature ORP Thermobond 65 performs very well in transverse deformation conditions.


TYPICAL PROPERTIES OF ORP THERMOBOND 65
Appearance:White powder
Chemical composition:VA / VeoVa / Acrylic Terpolymer
Stabilizing System:PVOH
Residual Humidity (%):Max. 1.5
Density (g/l):540 ± 70
Ash Content (%):12 ± 2
Alkali Resistance:High
After 1:1 Dispersion with Water:
pH:6.0 - 7.0
MFFT (°C):0

 

APPLICATION AREAS OF ORP THERMOBOND 65
ORP Thermobond 65 can be used in mortar formulations where good flexibility/elasticity, recovery and
thixotropic behavior is required.

EIFS (Exterior Insulation and Finishing Systems) Plasters:
Due to its excellent flexibility and water resistance, ORP Thermobond 65 can be used for
manufacturing of cementitious base coats applied on EPS&XPS boards in EIFS. The recommended
dosage: 3.0 - 5.0 %

Adhesives for EPS&XPS boards in EIFS:
The recommended dosages: 1.0 - 2.0 %

Tile Adhesives (S1 & S2):
The recommended dosages: 3.0 - 7.0 %

PRODUCT HANDLING - STORAGE - SHELFLIFE OF ORP THERMOBOND 65
Packaging: Pallet with 18 paper bags, each 25 kg (450 kg) or big bags (500 kg).
Packages must be stored in a dry and cool warehouse at temperatures between 10 - 25 °C. Pallets
must not be stacked on top of each other to avoid caking due to the thermoplasticity of the polymer.
Packing must be closed well after usage for protection against humidity and caking. It has to be used
within 6 months.