SASOLWAX 2528

SASOLWAX 2528

CAS No.: 63231-60-7
EC No.: 264-038-1

Synonyms:
SASOLWAX 2528; sasolwax 2528; MICROCRISTALLINA CERA; Floorwax; VANFRE HYP; VANFRE M; VANFRE UN; VANFRE VAM; Multiwax ML-445; Multiwax W-445; Multiwax W-835; Microcrystalline wax; Petroleum wax, microcrystalline; Wax, microcrystalline [NF]; EC 264-038-1; EINECS 264-038-1; Microcrystalline paraffin waxes and hydrocarbon waxes; Microcrystalline wax; UNII-XOF597Q3KY; Wax, microcrystalline; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; Paraffin waxes and Hydrocarbon waxes, microcryst.; 63231-60-7; D06324; Microcrystalline wax; Wax, microcrystalline (NF); 63231-60-7; Microcrystalline paraffin waxes and hydrocarbon waxes; Paraffin waxes and Hydrocarbon waxes, microcryst.; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; XOF597Q3KY; 63231-60-7; Microcrystalline wax; Petroleum wax, microcrystalline; Wax, microcrystalline [NF]; Paraffin waxes and Hydrocarbon waxes, microcryst.; EINECS 264-038-1; Microcrystalline paraffin waxes and hydrocarbon waxes; UNII-XOF597Q3KY; Wax, microcrystalline; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; EC 264-038-1; ewacera 28; microcrystalline paraffin waxes and hydrocarbon waxes; microcrystalline wax; Floorwax; Microcrystallinwax; Paraffinwaxesandhydrocarbonwaxes, microcryst; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; paraffinwaxesandhydrocarbonwaxes, microcryst.; MULTIWAX(TM) W-835; MULTIWAX180-M; MULTIWAX180-W; MULTIWAXX-145A; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; PARAFFIN IN PASTILLE FORM 51-53 PH EUR,B; PARAFFIN IN PASTILLE FORM 52-54 PH EUR,B; PARAFFIN IN BLOCK FORM 42-44 25 KG; PARAFFIN IN BLOCK FORM 46-48 1 KG; PARAFFIN IN PASTILLE FORM 56-58 PH EUR,B; PARAFFIN IN PASTILLE FORM 57-60 PH EUR,B; PARAFFIN IN BLOCK FORM 46-48 25 KG; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; PARAFFIN IN BLOCK FORM 42-44 1 KG; 64742-51-4; PARAFFIN PASTILLES 56-58 HISTOLO; Paraffin, solidification point 56 em leader58 degrees C, in pastille form for histology; 64742-51-4; Hydrotreated paraffin waxes (petroleum); SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; Paraffin waxes (petroleum), hydrotreated; 64742-51-4; Paraffin waxes, petroleum, hydrotreated; Paraffin waxes (petroleum), hydrotreated; EINECS 265-154-5; Hydrotreated paraffin wax; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; Hydrotreated paraffin waxes (petroleum); EC 265-154-5; Paraffin wax, hydrotreated; Paraffin waxes, (petroleum), hydrotreated; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; MICROCRISTALLINA CERA; Floorwax; VANFRE HYP; VANFRE M; VANFRE UN; VANFRE VAM; Multiwax ML-445; Multiwax W-445; Multiwax W-835; Microcrystalline wax; Petroleum wax, microcrystalline; Wax, microcrystalline [NF]; EC 264-038-1; EINECS 264-038-1; Microcrystalline paraffin waxes and hydrocarbon waxes; Microcrystalline wax; UNII-XOF597Q3KY; Wax, microcrystalline; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; Paraffin waxes and Hydrocarbon waxes, microcryst.; 63231-60-7; D06324; Microcrystalline wax; Wax, microcrystalline (NF); 63231-60-7; Microcrystalline paraffin waxes and hydrocarbon waxes; Paraffin waxes and Hydrocarbon waxes, microcryst.; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; XOF597Q3KY; 63231-60-7; Microcrystalline wax; Petroleum wax, microcrystalline; Wax, microcrystalline [NF]; Paraffin waxes and Hydrocarbon waxes, microcryst.; EINECS 264-038-1; Microcrystalline paraffin waxes and hydrocarbon waxes; UNII-XOF597Q3KY; Wax, microcrystalline; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; EC 264-038-1; ewacera 28; microcrystalline paraffin waxes and hydrocarbon waxes; microcrystalline wax; Floorwax; Microcrystallinwax; Paraffinwaxesandhydrocarbonwaxes, microcryst; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; paraffinwaxesandhydrocarbonwaxes, microcryst.; MULTIWAX(TM) W-835; MULTIWAX180-M; MULTIWAX180-W; MULTIWAXX-145A; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; PARAFFIN IN PASTILLE FORM 51-53 PH EUR,B; PARAFFIN IN PASTILLE FORM 52-54 PH EUR,B; PARAFFIN IN BLOCK FORM 42-44 25 KG; PARAFFIN IN BLOCK FORM 46-48 1 KG; PARAFFIN IN PASTILLE FORM 56-58 PH EUR,B; PARAFFIN IN PASTILLE FORM 57-60 PH EUR,B; PARAFFIN IN BLOCK FORM 46-48 25 KG; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; PARAFFIN IN BLOCK FORM 42-44 1 KG; 64742-51-4; PARAFFIN PASTILLES 56-58 HISTOLO; Paraffin, solidification point 56 em leader58 degrees C, in pastille form for histology; 64742-51-4; Hydrotreated paraffin waxes (petroleum); SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; Paraffin waxes (petroleum), hydrotreated; 64742-51-4; Paraffin waxes, petroleum, hydrotreated; Paraffin waxes (petroleum), hydrotreated; EINECS 265-154-5; Hydrotreated paraffin wax; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528; Hydrotreated paraffin waxes (petroleum); EC 265-154-5; Paraffin wax, hydrotreated; Paraffin waxes, (petroleum), hydrotreated; SASOLWAX 2528; sasolwax 2528; SASOLWAX 2528; sasolwax 2528


SASOLWAX 2528

Sasolwax 2528
Technical Datasheet | Supplied by Sasol in-cosmetics global 2020
Microcristallina Cera. Sasolwax 2528 by Sasol acts as a consistency regulator and oil binder. It is a multi-component blend of saturated hydrocarbons. It contains elevated content of iso- and cyclo-alkanes. It provides microcrystalline structure, ductility, smoothness and outstanding oil absorption capacity. It improves stability and adds structure & hardness to lip balm sticks and other products in stick form used as beauty products, without being excessively crystalline. Sasolwax 2528 is also used in creams and lotions. Meets European cosmetics regulation (No. 1223/2009) and Colipa: Recommendation No. 14 lip and oral care products.
Claims
SASOLWAX 2528 Waxes / Consistency Factors
SASOLWAX 2528 Thickeners & Stabilizers
SASOLWAX 2528 Binders
SASOLWAX 2528 absorption
SASOLWAX 2528 hardening
SASOLWAX 2528 smoothness
SASOLWAX 2528 INCI Names MICROCRISTALLINA CERA

Description

SASOLWAX 2528 is a medium melting point Fischer-Tropsch wax.It is available in flaked and pellet form .It is mostly used by intermediate companies who do wax grinding. SASOLWAX 2528 micronised ground form applied effectively in all areas where SASOLWAX 2528, SASOLWAX 2528 and SASOLWAX 2528 N4 are used.It is used as a viscosity regulator, melting point elevator in wax blends, lubricant and release agent in moulding and extrusion of plastic, insulating component in the cable,electrical industry and chewing gum base, in manufacture of carbon paper backing, crayons. Fischer-Tropsch high melting point wax available in coarse powder and pastille form. Sasol's Fischer-Tropsch hard waxes are synthetically produced by using gas-to-liquids (GTL) technology, in which Sasol is globally recognised as a commercial and technical pioneer. The GTL process uses natural gas to produce premium Fischer-Tropsch hard waxes. As a prime quality Fischer-Tropsch hard wax, SASOLWAX 2528 has been successfully established in EVA-based and metallocene polyolefin copolymer hot melt adhesive formulations. SASOLWAX 2528, the market standard for FT hard wax, provides a superior balance in adhesive performance and temperature stability. The linear molecule structure of SASOLWAX 2528 gives a hot melt adhesive the unique characteristics of low viscosity combined with high crystallinity, which ensures ideal performance properties in hot melt adhesives: Being highly compatible with typically used resins, EVA and metallocene polyolefin copolymers, SASOLWAX 2528 is ideally suited to the requirements of modern hot melt adhesives, particularly in packaging applications. SASOLWAX 2528 by Sasol is a fully hydrogenated Fischer-Tropsch hard wax. It is available as coarse powder or pastilles. It is composed of hydrocarbon chains that are predominantly linear. It has high melting point, low viscosity, excellent hardness and has good heat stability. The linear molecule structure of SASOLWAX 2528 gives a hot melt adhesive the unique characteristics of low viscosity combined with high crystallinity, which ensures ideal performance properties in hot melt adhesives. Being highly compatible with typically used resins, EVA and metallocene polyolefin copolymers, SASOLWAX 2528 is ideally suited to the requirements of modern hot melt adhesives, particularly in packaging applications. SASOLWAX 2528 complies with European specifications for food additives according to E905, FDA CFR 21, Commission Regulation (EU) No 10/2011 (Ref. 95859), Recommendation of the BfR (German Federal Institute for Risk Assessment) XXV, Part C. SASOLWAX 2528 improves the degassing of powder coatings during the extrusion process. With H1 is easy eliminate the bubbles in the melt powder coating or remove coating film pinhole. This product is suitable for all types of powder coating systems (polyester/TGIC/Beta-HAA/epoxy-functional glycidyl esters,polyester/epoxy, polyurethane, acrylate, and epoxy).Synthetic wax made by the Fischer-Tropsch process. Possesses similar structure to paraffin wax, higher melting point, hardness and molecular weight. Used in hot melt adhesives. The influence of three different waxes on the thermal and mechanical properties of linear low-density polyethylene (LLDPE) was investigated. The samples were prepared through melt blending in a Brabender mixer. The thermal properties of the samples were determined using differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA). The tensile and flow properties of all the samples were determined and compared. The polymer-wax miscibilities differed with the type of wax used, and with the amount of wax mixed into the polymer. These miscibilities, and accompanying morphologies, had a strong influence on the flow properties, thermal stabilities and tensile properties of the corresponding blends. H1 wax and M3 wax (which are both Fischer-Tropsch paraffin waxes produced by Sasol Wax) both reduce the apparent viscosity of LLDPE more than EnHance (a Fischer-Tropsch paraffin wax produced by Sasol Wax as a polyethylene processing lubricant). M3 wax had the strongest influence on the melt flow rates (MFI) of the blends, and it had the least influence on the tensile properties of LLDPE. It did, however, strongly reduce its thermal stability. H1 wax, on the other hand, had only a small influence on the thermal stability of LLDPE, but like EnHance it strongly increased the modulus. Fischer-Tropsch wax, available as white pellets. SASOLWAX 2528 has straight chain of hydrocarbons, a high melting point, a low viscosity, an excellent hardness and is stable. It complies with FDA & BGA. Sasol's Fischer-Tropsch hard waxes are synthetically produced by using gas-to-liquids (GTL) technology, in which Sasol is globally recognised as a commercial and technical pioneer. The GTL process uses natural gas to produce premium Fischer-Tropsch hard waxes. SASOLWAX 2528 has been widely proven in the industry as being an excellent external lubricant for use during PVC processing. The linear molecule structure and the low viscosity of SASOLWAX 2528 ensure ideal processing of the PVC material by:
• Efficiently controlling the fusion of PVC by increasing the fusion time and reducing the fusion torque
• Providing a metal release effect by preventing the PVC melt from sticking on the metal surface
• Allowing for exceptional consistency in batch processes
• Reducing the formation of hot spots resulting in thermal degradation
• Improving surface gloss
• Reducing energy consumption
• Increasing production yield, reduces scrap

Microcrystalline waxes are a type of wax produced by de-oiling petrolatum, as part of the petroleum refining process. In contrast to the more familiar paraffin wax which contains mostly unbranched alkanes, microcrystalline wax contains a higher percentage of isoparaffinic (branched) hydrocarbons and naphthenic hydrocarbons. It is characterized by the fineness of its crystals in contrast to the larger crystal of paraffin wax. It consists of high molecular weight saturated aliphatic hydrocarbons. It is generally darker, more viscous, denser, tackier and more elastic than paraffin waxes, and has a higher molecular weight and melting point. The elastic and adhesive characteristics of microcrystalline waxes are related to the non-straight chain components which they contain. Typical microcrystalline wax crystal structure is small and thin, making them more flexible than paraffin wax. It is commonly used in cosmetic formulations. Microcrystalline waxes when produced by wax refiners are typically produced to meet a number of ASTM specifications. These include congeal point (ASTM D938), needle penetration (D1321), color (ASTM D6045), and viscosity (ASTM D445). Microcrystalline waxes can generally be put into two categories: "laminating" grades and "hardening" grades. The laminating grades typically have a melt point of 140-175 F (60 - 80 oC) and needle penetration of 25 or above. The hardening grades will range from about 175-200 F (80 - 93 oC), and have a needle penetration of 25 or below. Color in both grades can range from brown to white, depending on the degree of processing done at the refinery level. Microcrystalline waxes are derived from the refining of the heavy distillates from lubricant oil production. This by-product must then be de-oiled at a wax refinery. Depending on the end use and desired specification, the product may then have its odor removed and color removed (which typically starts as a brown or dark yellow). This is usually done by means of a filtration method or by hydro-treating the wax material.
 
Industries and Applications
Microcrystalline wax is often used in industries such as tire and rubber, candles, adhesives, corrugated board, cosmetics, castings, and others. Refineries may use blending facilities to combine paraffin and microcrystalline waxes; this is prevalent in the tire and rubber industries. Microcrystalline waxes have considerable application in the custom making of jewelry and small sculptures. Different formulations produce waxes from those soft enough to be molded by hand to those hard enough to be carved with rotary tools. The melted wax can be cast to make multiple copies that are further carved with details. Jewelry suppliers sell wax molded into the basic forms of rings as well as details that can be heat welded together and tubes and sheets for cutting and building the wax models. Rings may be attached to a wax "tree" so that many can be cast in one pouring. A brand of microcrystalline wax, Renaissance Wax, is also used extensively in museum and conservation settings for protection and polishing of antique woods, ivory, gemstones, and metal objects. It was developed by The British Museum in the 1950s to replace the potentially unstable natural waxes that were previously used such as beeswax and carnauba. Microcrystalline waxes are excellent materials to use when modifying the crystalline properties of paraffin wax. The microcrystalline wax has significantly more branching of the carbon chains that are the backbone of paraffin wax. This is useful when some desired functional changes in the paraffin are needed, such as flexibility, higher melt point, and increased opacity. They are also used as slip agents in printing ink. Microcrystalline wax is used in such sports as ice hockey and snowboarding. It is applied to the friction tape of an ice hockey stick to prevent degradation of the tape due to water destroying the glue on the tape and also to increase control of the hockey puck due to the wax's adhesive quality. It is also applied to the underside of snowboards to reduce friction and increase the gliding ability of the board, making it easier to control. Microcrystalline wax was used in the final phases of the restoration of the Cosmatesque pavement, Westminster Abbey, London.

Use in Petrolatum
Microcrystalline wax is also a key component in the manufacture of petrolatum. The branched structure of the carbon chain backbone allows oil molecules to be incorporated into the crystal lattice structure. The desired properties of the petrolatum can be modified by using microcrystalline wax bases of different congeal points (ASTM test D938) and needle penetration (ASTM D1321). However, key industries that utilize petrolatum, such as the personal care, cosmetic, and candle industries, have pushed for more materials that are considered "green" and based on renewable resources. As an alternative, hybrid petrolatum can be used. Hybrid petrolatum utilizes a complex mixture of vegetable oils and waxes and combines them with petroleum and micro wax based technologies. This allows a formulator to incorporate higher percentages of renewable resources while maintaining the beneficial properties of the petrolatum.

SASOLWAX 2528 Chemical Properties
SASOLWAX 2528 Melting Point: 205°C
SASOLWAX 2528 Molar Mass: 750 g/mol
SASOLWAX 2528 Viscosity: 8 cPs
SASOLWAX 2528 Congealing point °C: 97
SASOLWAX 2528 Drop melting point °C: 112
SASOLWAX 2528 Brookfield viscosity at 135°C: 8
SASOLWAX 2528 Penetration: At 25 °C : max 1
SASOLWAX 2528 Penetration at 65 °C : max 18
SASOLWAX 2528 Colour Saybolt :+ 22
SASOLWAX 2528 Oil content: < 0.2
SASOLWAX 2528 Molecular weight Dalton : - 880
SASOLWAX 2528 n-Alkanes: % 90.6 
SASOLWAX 2528 Alpha-olefins: % 0.1 
SASOLWAX 2528 Iso-alkanes: % 7.4 
SASOLWAX 2528 Alcohols: % 0.4 
SASOLWAX 2528 Other: % 1.5 
SASOLWAX 2528 Total recovery: % 74.9 
Molecular weight Mn, dalton: 746 
Average carbon number based on Mn: C53 
Molecular weight Mw, dalton: 853 
Average carbon number based on Mw: C61 
DSC melting maxima, °C: 84/105 
Contents: 100.00 %W/W
Form: Coarse powder
State of matter: Solid; at 20 °C; 1,013 hPa
Color:White to colourless
Odour: Odourless
Melting point/range: 45 - 75 °C
Boiling point/boiling range: > 200 °C
Flash point / Evaporation rate : > 200 °C
Relative vapour density: 0.9 g/cm3; 25 °C
 
The specifications of SASOLWAX 2528 are secured through our highly developed production technology. The management system including production is certified according to ISO 9001, ISO 14001 and OHSAS 18001. SASOLWAX 2528 complies with the following regulations: 
• FDA CFR 21:
§172.615 "Chewing Gum Base"
§175.105 "Adhesives"
§175.250 "Paraffin (synthetic)"
§175.300 "Resinous and polymeric coatings"
§175.320 "Resinous and polymeric coatings for polyolefin films"
§176.170 "Components of paper and paperboard in contact with aqueous and fatty foods"
§176.180 "Components of paper and paperboard in contact with dry food"
§177.1200 "Cellophane"
§177.1390 "Laminate structures for use at temperatures of 250 °F and above"
• Commission Regulation (EU) No 10/2011 on plastic materials and articles intended
to come into contact with food: product is in compliance with the specification of Ref.
No. 95859 Waxes, refined, derived from petroleum based or synthetic hydrocarbon
feedstocks, high viscosity.
• Recommendation of the BfR (German Federal Institute for Risk Assessment) XXV,
Part C, (Synthetische Hartparaffine)
• European specifications for food additives according to E905
Substance: Synthetic wax, Paraffinic hydrocarbons

Application

SASOLWAX 2528 is ideal for blending with high priced grades such as PTFE. Processed for use in: Lithographic heat set inks / Water based liquid inks / Wax blend component
-Hot melt adhesives
-Polishes
-Beads and scrubs
-Mould release
-Adhesives
-Household and consumer goods
-Cosmetics
-Personal care
-Suitable for various other applications
Suitable extinguishing agents:
-Use fire extinguishing methods suitable to surrounding conditions.
-Water haze
-Water spray
-Foam
-Fire-extinguishing powder
-Carbon dioxide
-Sand
Description of first aid measures
General information: No special measures required.
After inhalation: Supply fresh air; consult doctor in case of complaints.
After skin contact: After contact with the molten product, cool rapidly with cold water.
After eye contact: Rinse opened eye for several minutes under running water.
After swallowing: If symptoms persist consult doctor.


SASOLWAX 2528

Sasolwax 2528
Teknik Veri Sayfası | Sasol in-kozmetik global 2020 tarafından tedarik edilmektedir
Microcristallina Cera. Sasol tarafından üretilen Sasolwax 2528, kıvam düzenleyici ve yağ bağlayıcı görevi görür. Çok bileşenli doymuş hidrokarbon karışımıdır. Yüksek izo- ve siklo-alkan içeriği içerir. Mikrokristal yapı, süneklik, pürüzsüzlük ve olağanüstü yağ emme kapasitesi sağlar. Dudak kremi çubuklarına ve güzellik ürünleri olarak kullanılan çubuk şeklindeki diğer ürünlere aşırı kristalleşmeden stabiliteyi artırır ve yapı ve sertlik kazandırır. Sasolwax 2528 krem ve losyonlarda da kullanılmaktadır. Avrupa kozmetik yönetmeliğini (No. 1223/2009) ve Colipa: Öneri No. 14 dudak ve ağız bakım ürünlerini karşılar.
İddialar
SASOLWAX 2528 Vakslar / Tutarlılık Faktörleri
SASOLWAX 2528 Yoğunlaştırıcılar ve Stabilizatörler
SASOLWAX 2528 Bağlayıcılar
SASOLWAX 2528 emilimi
SASOLWAX 2528 sertleştirme
SASOLWAX 2528 pürüzsüzlük
SASOLWAX 2528 INCI İsimler MICROCRISTALLINA CERA

Açıklama

SASOLWAX 2528 orta erime noktalı bir Fischer-Tropsch mumudur.Pullanılmış ve pelet şeklinde mevcuttur.Çoğunlukla balmumu öğütme yapan ara firmalar tarafından kullanılır. SASOLWAX 2528 mikronize zemin formu, SASOLWAX 2528, SASOLWAX 2528 ve SASOLWAX 2528 N4'ün kullanıldığı tüm alanlarda etkin bir şekilde uygulanmaktadır.Viskozite düzenleyici, mum karışımlarında erime noktası yükseltici, plastiğin kalıplama ve ekstrüzyonunda yağlayıcı ve ayırıcı olarak kullanılır, izolasyon kablo, elektrik endüstrisi ve sakız mayasındaki bileşen, karbon kağıt destek, boya kalemi üretiminde. Fischer-Tropsch yüksek erime noktalı mum, kaba toz ve pastil formunda mevcuttur. Sasol'ün Fischer-Tropsch sert mumları, Sasol'un dünya çapında ticari ve teknik bir öncü olarak kabul edildiği, gazdan sıvıya (GTL) teknolojisi kullanılarak sentetik olarak üretilir. GTL işlemi, birinci sınıf Fischer-Tropsch sert mumlarını üretmek için doğal gaz kullanır. Birinci sınıf bir Fischer-Tropsch sert mumu olarak SASOLWAX 2528, EVA bazlı ve metalosen poliolefin kopolimer sıcakta eriyen yapışkan formülasyonlarında başarıyla kurulmuştur. FT sert mum için pazar standardı olan SASOLWAX 2528, yapıştırıcı performansında ve sıcaklık kararlılığında üstün bir denge sağlar. SASOLWAX 2528'in doğrusal molekül yapısı, sıcak eriyik yapıştırıcıya, sıcak eriyik yapıştırıcılarda ideal performans özelliklerini sağlayan, yüksek kristallik ile birlikte düşük viskozitenin benzersiz özelliklerini verir: Tipik olarak kullanılan reçineler, EVA ve metalosen poliolefin kopolimerleri ile son derece uyumlu olan SASOLWAX 2528, özellikle ambalaj uygulamalarında modern hot melt yapıştırıcıların gereksinimlerine ideal olarak uygundur. SASOLWAX 2528 by Sasol, tamamen hidrojene edilmiş bir Fischer-Tropsch sert mumudur. Kaba toz veya pastil olarak mevcuttur. Ağırlıklı olarak doğrusal olan hidrokarbon zincirlerinden oluşur. Yüksek erime noktasına, düşük viskoziteye, mükemmel sertliğe ve iyi ısı stabilitesine sahiptir. SASOLWAX 2528'in doğrusal molekül yapısı, sıcakta eriyen yapıştırıcıya, yüksek kristallik ile birlikte düşük viskozitenin benzersiz özelliklerini verir, bu da sıcakta eriyen yapıştırıcılarda ideal performans özellikleri sağlar. Tipik olarak kullanılan reçineler, EVA ve metalosen poliolefin kopolimerleri ile oldukça uyumlu olan SASOLWAX 2528, özellikle ambalaj uygulamalarında modern sıcak eriyik yapıştırıcıların gereksinimlerine ideal olarak uygundur. SASOLWAX 2528, E905, FDA CFR 21, Komisyon Yönetmeliği (AB) No. 10/2011 (Ref. 95859), BfR Tavsiyesi (Alman Federal Risk Değerlendirme Enstitüsü) XXV, Bölüm C. SASOLWAX uyarınca gıda katkı maddeleri için Avrupa spesifikasyonlarına uygundur. 2528, ekstrüzyon işlemi sırasında toz kaplamaların gazdan arındırılmasını iyileştirir. H1 ile eriyik toz kaplamadaki kabarcıkları ortadan kaldırmak veya kaplama filmi iğne deliğini çıkarmak kolaydır. Bu ürün, her tür toz boya sistemi için uygundur (polyester / TGIC / Beta-HAA / epoksi-fonksiyonel glisidil esterler, polyester / epoksi, poliüretan, akrilat ve epoksi). Fischer-Tropsch işlemi ile yapılan sentetik mum. Parafin mumuna benzer yapıya, daha yüksek erime noktasına, sertliğe ve moleküler ağırlığa sahiptir. Sıcakta eriyen yapıştırıcılarda kullanılır. Üç farklı mumun doğrusal düşük yoğunluklu polietilenin (LLDPE) termal ve mekanik özellikleri üzerindeki etkisi araştırıldı. Numuneler, bir Brabender mikserinde eriyik harmanlama yoluyla hazırlandı. Numunelerin termal özellikleri diferansiyel taramalı kalorimetri (DSC) ve termogravimetrik analiz (TGA) kullanılarak belirlendi. Tüm numunelerin çekme ve akış özellikleri belirlenmiş ve karşılaştırılmıştır. Polimer balmumu karışabilirlikleri, kullanılan balmumu tipine ve polimere karıştırılan balmumunun miktarına göre farklılık gösterdi. Bu karışıklıklar ve bunlara eşlik eden morfolojiler, karşılık gelen karışımların akış özellikleri, termal stabiliteleri ve gerilme özellikleri üzerinde güçlü bir etkiye sahipti. H1 balmumu ve M3 balmumu (her ikisi de Sasol Wax tarafından üretilen Fischer-Tropsch parafin mumlarıdır), LLDPE'nin görünür viskozitesini EnHance'den (Sasol Wax tarafından bir polietilen işleme yağlayıcı olarak üretilen bir Fischer-Tropsch parafin mumu) daha fazla azaltır. M3 mumu, harmanların eriyik akış hızları (MFI) üzerinde en güçlü etkiye sahipti ve LLDPE'nin gerilme özellikleri üzerinde en az etkiye sahipti. Bununla birlikte, termal stabilitesini büyük ölçüde azalttı. Öte yandan H1 mumunun LLDPE'nin termal stabilitesi üzerinde sadece küçük bir etkisi vardı, ancak EnHance gibi modülü güçlü bir şekilde arttırdı. Fischer-Tropsch mumu, beyaz topaklar halinde mevcuttur. SASOLWAX 2528, düz hidrokarbon zincirine, yüksek erime noktasına, düşük viskoziteye, mükemmel sertliğe sahiptir ve kararlıdır. FDA ve BGA ile uyumludur. Sasol'ün Fischer-Tropsch sert mumları, Sasol'un dünya çapında ticari ve teknik bir öncü olarak kabul edildiği, gazdan sıvıya (GTL) teknolojisi kullanılarak sentetik olarak üretilir. GTL işlemi, birinci sınıf Fischer-Tropsch sert mumlarını üretmek için doğal gaz kullanır.
SASOLWAX 2528, PVC işleme sırasında kullanım için mükemmel bir harici yağlayıcı olarak endüstride geniş çapta kanıtlanmıştır. SASOLWAX 2528'in doğrusal molekül yapısı ve düşük viskozitesi, PVC malzemenin aşağıdaki yöntemlerle ideal şekilde işlenmesini sağlar:
• Füzyon süresini artırarak ve füzyon torkunu azaltarak PVC'nin füzyonunu verimli bir şekilde kontrol etme
• PVC eriyiğinin metal yüzeye yapışmasını engelleyerek metal ayırma etkisi sağlamak
• Toplu işlemlerde olağanüstü tutarlılığa izin verme
• Termal bozulmaya neden olan sıcak noktaların oluşumunu azaltmak
• Yüzey parlaklığını iyileştirme
• Enerji tüketimini azaltmak
• Üretim verimini arttırır, hurdayı azaltır

Mikrokristalin mumlar, petrol arıtma işleminin bir parçası olarak petrolatumun yağdan arındırılmasıyla üretilen bir mum türüdür. Çoğunlukla dallanmamış alkanlar içeren daha bilinen parafin mumunun aksine, mikrokristalin mum daha yüksek oranda izoparafinik (dallı) hidrokarbonlar ve naftenik hidrokarbonlar içerir. Daha büyük olan parafin balmumu kristalinin aksine kristallerinin inceliği ile karakterizedir. Yüksek moleküler ağırlıklı doymuş alifatik hidrokarbonlardan oluşur. Genellikle parafin mumlarına göre daha koyu, daha viskoz, daha yoğun, daha yapışkan ve daha elastiktir ve daha yüksek moleküler ağırlığa ve erime noktasına sahiptir. Mikrokristalin mumların elastik ve yapışkan özellikleri, içerdikleri düz olmayan zincir bileşenleri ile ilgilidir. Tipik mikrokristalin balmumu kristal yapısı küçük ve incedir, bu da onları parafin mumundan daha esnek kılar. Genellikle kozmetik formülasyonlarda kullanılır. Mumlu rafineriler tarafından üretildiklerinde mikrokristalin mumlar tipik olarak bir dizi ASTM spesifikasyonunu karşılayacak şekilde üretilir. Bunlar donma noktası (ASTM D938), iğne penetrasyonu (D1321), renk (ASTM D6045) ve viskoziteyi (ASTM D445) içerir. Mikrokristalin mumlar genellikle iki kategoriye ayrılabilir: "laminasyon" dereceleri ve "sertleştirme" dereceleri. Laminasyon sınıfları tipik olarak 140-175 F (60 - 80 oC) erime noktasına ve 25 veya üzerinde iğne penetrasyonuna sahiptir. Sertleştirme dereceleri yaklaşık 175-200 F (80 - 93 oC) arasında değişecek ve 25 veya altında bir iğne girişine sahip olacaktır. Her iki sınıftaki renk, rafineri düzeyinde yapılan işleme derecesine bağlı olarak kahverengiden beyaza kadar değişebilir. Mikrokristalin mumlar, yağlama yağı üretiminden elde edilen ağır damıtıkların rafine edilmesinden elde edilir. Bu yan ürün daha sonra bir balmumu rafinerisinde yağdan arındırılmalıdır. Nihai kullanıma ve istenen spesifikasyona bağlı olarak, ürünün kokusu giderilebilir ve rengi giderilebilir (tipik olarak kahverengi veya koyu sarı olarak başlar). Bu genellikle bir filtrasyon yöntemi ile veya balmumu malzemesinin hidro-muameleye tabi tutulmasıyla yapılır.
 
Sektörler ve Uygulamalar
Mikrokristalin balmumu genellikle lastik ve kauçuk, mumlar, yapıştırıcılar, oluklu mukavva, kozmetikler, dökümler ve diğerleri gibi endüstrilerde kullanılır. Rafineriler, parafin ve mikrokristalin mumları birleştirmek için harmanlama tesisleri kullanabilir; bu, lastik ve kauçuk endüstrisinde yaygındır. Mikrokristalin mumlar, özel takı ve küçük heykel yapımında önemli bir uygulamaya sahiptir. Farklı formülasyonlar, elle kalıplanacak kadar yumuşak olanlardan, döner aletlerle oyulabilecek kadar sert olanlara kadar mumlar üretir. Erimiş balmumu, detaylarla daha fazla oyulmuş birden fazla kopya yapmak için dökülebilir. Kuyumculuk tedarikçileri, temel halka biçimlerinde kalıplanmış balmumunun yanı sıra, birlikte ısıyla kaynaklanabilen detaylar ve balmumu modellerini kesmek ve oluşturmak için tüpler ve levhalar satmaktadır. Halkalar bir balmumu "ağacına" tutturulabilir, böylece birçoğu tek bir dökümde dökülebilir. Bir mikrokristalin balmumu markası olan Renaissance Wax, antika ahşapların, fildişinin, değerli taşların ve metal nesnelerin korunması ve cilalanması için müze ve koruma ortamlarında da yaygın olarak kullanılmaktadır. 1950'lerde British Museum tarafından daha önce kullanılan balmumu ve karnauba gibi potansiyel olarak kararsız doğal mumların yerini almak için geliştirildi. Mikrokristalin mumlar, parafin mumunun kristal özelliklerini değiştirirken kullanmak için mükemmel malzemelerdir. Mikrokristalin mum, parafin mumunun omurgası olan karbon zincirlerinde önemli ölçüde daha fazla dallanmaya sahiptir. Bu, esneklik, daha yüksek erime noktası ve artan opaklık gibi parafinde istenen bazı fonksiyonel değişikliklere ihtiyaç duyulduğunda yararlıdır. Ayrıca matbaa mürekkebinde kaydırıcı olarak kullanılırlar. Mikrokristalin balmumu buz hokeyi ve snowboard gibi sporlarda kullanılır. Bant üzerindeki yapıştırıcıyı tahrip eden sudan dolayı bandın bozulmasını önlemek ve ayrıca balmumunun yapışkan kalitesinden dolayı hokey diskinin kontrolünü arttırmak için buz hokeyi sopasının sürtünme bandına uygulanır. Sürtünmeyi azaltmak ve tahtanın kayma kabiliyetini arttırmak için snowboardların alt tarafına da uygulanarak kontrolü kolaylaştırır. Londra'daki Westminster Abbey'deki Cosmatesque kaplamasının restorasyonunun son aşamalarında mikrokristalin balmumu kullanıldı.

Petrolatum'da kullanın
Mikrokristalin balmumu da vazelin üretiminde önemli bir bileşendir. Karbon zincir omurgasının dallı yapısı, yağ moleküllerinin kristal kafes yapısına dahil edilmesine izin verir. Petrolatumun istenen özellikleri, farklı donma noktalarına (ASTM testi D938) ve iğne penetrasyonuna (ASTM D1321) sahip mikrokristalin balmumu bazları kullanılarak değiştirilebilir. Ancak, kişisel bakım, kozmetik ve mum endüstrileri gibi petrolatumu kullanan kilit endüstriler, "yeşil" kabul edilen ve yenilenebilir kaynaklara dayalı daha fazla malzeme için baskı yaptı. Alternatif olarak hibrit vazelin kullanılabilir. Hibrit vazelin, karmaşık bir bitkisel yağ ve mum karışımını kullanır ve bunları petrol ve mikro mum bazlı teknolojilerle birleştirir. Bu, bir formülatörün, petrolatumun yararlı özelliklerini korurken, yenilenebilir kaynakların daha yüksek yüzdelerini dahil etmesine izin verir.

SASOLWAX 2528 Kimyasal Özellikler
SASOLWAX 2528 Erime Noktası: 205 ° C
SASOLWAX 2528 Molar Kütle: 750 g / mol
SASOLWAX 2528 Viskozite: 8 cPs
SASOLWAX 2528 Donma noktası ° C: 97
SASOLWAX 2528 Damla erime noktası ° C: 112
SASOLWAX 2528 Brookfield viskozitesi, 135 ° C'de: 8
SASOLWAX 2528 Penetrasyon: 25 ° C'de: en fazla 1
SASOLWAX 2528 65 ° C'de Penetrasyon: maks 18
SASOLWAX 2528 Renkli Saybolt: + 22
SASOLWAX 2528 Yağ içeriği: <0.2
SASOLWAX 2528 Molekül ağırlığı Dalton: - 880
SASOLWAX 2528 n-Alkanlar:% 90.6
SASOLWAX 2528 Alfa-olefinler:% 0.1
SASOLWAX 2528 İzo-alkanlar:% 7.4
SASOLWAX 2528 Alkoller:% 0.4
SASOLWAX 2528 Diğer:% 1.5
SASOLWAX 2528 Toplam kurtarma:% 74.9
Moleküler ağırlık Mn, dalton: 746
Mn: C53'e dayalı ortalama karbon sayısı
Molekül ağırlığı Mw, dalton: 853
Mw'ye göre ortalama karbon sayısı: C61
DSC erime maksimum, ° C: 84/105
İçerik:% 100.00 W / W
Form: Kaba toz
Maddenin durumu: Katı; 20 ° C'de; 1.013 hPa
Renk: Beyazdan renksiz
Koku: Kokusuz
Erime noktası / aralığı: 45-75 ° C
Kaynama noktası / kaynama aralığı:> 200 ° C
Parlama noktası / Buharlaşma hızı:> 200 ° C
Nispi buhar yoğunluğu: 0,9 g / cm3; 25 ° C
 
SASOLWAX 2528'in teknik özellikleri, son derece gelişmiş üretim teknolojimiz ile güvence altına alınmıştır. Üretim dahil yönetim sistemi ISO 9001, ISO 14001 ve OHSAS 18001'e göre sertifikalandırılmıştır. SASOLWAX 2528 aşağıdaki yönetmeliklere uygundur:
• FDA CFR 21:
§172.615 "Sakız Bazı"
§175.105 "Yapıştırıcılar"
§175.250 "Parafin (sentetik)"
§175.300 "Reçineli ve polimerik kaplamalar"
§175.320 "Poliolefin filmler için reçineli ve polimerik kaplamalar"
§176.170 "Sulu ve yağlı yiyeceklerle temas halindeki kağıt ve karton bileşenleri"
§176.180 "Kuru gıda ile temas eden kağıt ve karton bileşenleri"
§177.1200 "Selofan"
§177.1390 ​​"250 ° F ve üzeri sıcaklıklarda kullanım için laminat yapılar"
• Komisyon Yönetmeliği (AB) 10/2011 sayılı plastik malzemeler ve amaçlanan eşyalar
gıda ile temas etmek için: ürün, Ref.
95859 Petrol bazlı veya sentetik hidrokarbondan elde edilen rafine mumlar
hammaddeler, yüksek viskozite.
• BfR (Alman Federal Risk Değerlendirme Enstitüsü) XXV'nin Tavsiyesi,
Bölüm C, (Synthetische Hartparaffine)
• E905'e göre gıda katkı maddeleri için Avrupa spesifikasyonları
Madde: Sentetik mum, Parafinik hidrokarbonlar

Uygulama

SASOLWAX 2528, PTFE gibi yüksek fiyatlı kalitelerle harmanlamak için idealdir. Aşağıdakilerde kullanım için işlenmiştir: Litografik ısıyla sertleşen mürekkepler / Su bazlı sıvı mürekkepler / Balmumu karışımı bileşeni
-Hot eriyen yapıştırıcılar
- Cilalar
Boncuklar ve önlükler
-Salıverilebilir
Yapıştırıcılar
-Ev ve tüketim malları
-Makyaj malzemeleri
-Kişisel Bakım
Çeşitli diğer uygulamalar için uygundur
Uygun söndürme maddeleri:
-Çevre koşullarına uygun yangın söndürme yöntemlerini kullanın.
-Su sisi
-Su spreyi
-Köpük
-Yangın söndürme tozu
-Karbon dioksit
-Kum
İlk yardım önlemlerinin açıklaması
Genel bilgi: Özel önlem gerekmez.
Teneffüs ettikten sonra: Temiz hava sağlayın; şikayet durumunda doktora başvurunuz.
Cilt temasından sonra: Erimiş ürünle temas ettikten sonra soğuk suyla hızla soğutun.
Göz temasından sonra: Açık gözü akan su altında birkaç dakika yıkayın.
Yuttuktan sonra: Belirtiler devam ederse doktora başvurun.
Ataman Chemicals © 2015 All Rights Reserved.