POWDER POLYMERS

Redispersible polymer powders
Organik Kimya's construction solutions meet the highest demands as the demanding and ever-changing construction market continues to evolve.
Polymer emulsions ORGAL ® and powder polymers ORP ® offer a range of solutions for the production of dry mixes and other building materials.


REDISPERSIBLE POLYMER POWDERS
DESCRIPTION
Redispersible polymer powder

Synonyms : RPP, polymer powder, polymer additive, RDP
Redispersible polymer powder (RPP) is a polymer capable, when mixed with water, to redisperse, again form aqueous polymer dispersions, which, as a result of curing, form a continuous polymer film, contributing to high water-holding capacity, adhesion and workability of dry building mixtures. 

Production method
The redispersible powder is obtained by spray drying a latex emulsion. To prevent the latex particles from sticking together during production and when diluted with water, polyvinyl alcohol is used. RPP (dry latexes) are usually produced on the basis of: polyvinyl acetate, copolymers of vinyl acetate with ethylene, copolymers of vinyl acetate with vinyl versatate, as well as acrylic polymers.

Properties
After mixing the dry mixture with water, the powder goes into dispersion and after drying forms a film. The film increases adhesion and elasticity, however, the more adhesion, the less elasticity and vice versa. Accordingly, powders are divided into rigid ones with high adhesion, highly elastic with low adhesion, and medium elastic with normal adhesion. In some powders, water repellents are added, imparting hydrophobic properties to the system.

Application area
Redispersible polymer powders are used in the manufacture of products such as:

- Tile adhesives; 
- Plasters; 
- Putties;
- Repair compositions; 
- Waterproofing; 
- Self-leveling floors, etc. 

Organik kimya
ORP 6072 MP
ORP 7085 HM
ORP 7090 RD
ORP 7099 RD
ORP 7365 HP
ORP 7680 SL
ORP Hydroflex 64
ORP Thermobond 45
ORP Thermobond 65
ORP Thermobond 74



ORP 6072 MP
ORP 6072 MP is a redispersible powder obtained by drying a Vinyl Acetate / Vinyl Versatate / Acrylic Terpolymer emulsion with PVA as a protective colloid. The specific chemical composition of the polymer ensures the coalescence of the redispersible polymer at low temperatures and ensures good adhesion to various substrates.
ORP 6072 MP is used for modifying mixtures containing various binders. Due to its special physical / chemical composition, ORP 6072 MP improves the adhesion, flexibility and water resistance of mortars containing cement, gypsum or lime. ORP 6072 MP provides excellent performance after heat aging and immersion in water.
Recommended area of ​​application
Tile adhesive C1: 0.5 - 1.0%
Tile adhesive C2: 2.0 - 5.0%
Adhesive for SFTK: 1.0 - 2.0%

Product properties
Chemical base VinylAcetate / VinylVersatate / Acrylic Terpolymer (VA / VV / Acrylic Terpolymer)
Minimum foaming temperature 8 ± 1 C
Ash content at 600 C 14 ± 2%
Bulk density 400-600 kg / m3
Characteristics
Due to its strong adhesion properties, ORP 6072 MP can be used for the production of tile adhesives and SFTK adhesives that fully comply with the requirements of the standards.
With excellent adhesion, abrasion and moisture resistance, ORP 6072 MP can be used in grouting and repair mortars ranging from 2.0 to 4.0%.
Due to its excellent water resistance and compressive strength, ORP 6072 MP can also be used in SFTK plasters, from 3.0 to 5.0%.



ORP 7085 HM
ORP 7085 HM is a redispersible powder obtained by drying a Vinyl Acetate / Acrylic copolymer emulsion with PVA as a protective colloid. The specific chemical composition of the polymer ensures the coalescence of the redispersible polymer at low temperatures and ensures good adhesion to various substrates. ORP 7085 HM is used to modify mixtures containing various binders.
Recommended area of ​​application
Tile adhesive C1: 0.5 - 1.0%
Tile adhesive C2: 2.0 - 5.0%

Product properties
Chemical base VinylAcetate / Acrylic Copolymer (VA / Acrylic Copolymer)
Minimum foaming temperature 7 ± 1 C
Ash content at 600 C 12 ± 2%
Bulk density 350-550 kg / m3
Characteristics
Due to its high adhesion properties, ORP 7085 HM can be used for the production of tile adhesives that fully meet the C1 and C2 requirements.
With excellent adhesion, abrasion and water resistance, ORP 7085 HM can be used in repair mortars at a dosage of 1.0 - 2.0%.



ORP 7090 RD
ORP 7090 RD is a redispersible powder obtained by drying a Vinyl Acetate / Acrylic Copolymer emulsion with PVA as a protective colloid. The specific chemical composition of the polymer ensures the coalescence of the redispersible polymer at low temperatures and ensures good adhesion to various substrates.
ORP 7090 RD is used for modifying mixtures containing various binders. Due to its special physical / chemical composition, ORP 7090 RD improves the adhesion, flexibility and water resistance of mortars containing cement, gypsum or lime.
Recommended area of ​​application
Tile adhesive C1: 0.5 - 1.0%
Tile adhesive C2: 2.0 - 5.0%

Product properties
Chemical base VinylAcetate / Acrylic Copolymer (VA / Acrylic Copolymer)
Minimum foaming temperature 8 ± 1 C
Ash content at 600 C 12 ± 2%
Bulk density 400-600 kg / m3
Characteristics
Due to its high adhesive properties, ORP 7090 RD can be used for the production of tile adhesives that are fully compliant with C1 and C2 requirements.
With excellent adhesion, abrasion and water resistance, ORP 7090 RD can be used in repair mortars at a dosage of 1.0 - 2.0%.




ORP 7099 RD
RP 7099 RD is a redispersible powder obtained by drying a Vinyl Acetate / Acrylic copolymer emulsion with PVA as a protective colloid. The specific chemical composition of the polymer ensures the coalescence of the redispersible polymer at low temperatures and ensures good adhesion to various substrates.
ORP 7099 RD is used for modifying mixtures containing various binders. Due to its special physical / chemical composition, ORP 7099 RD improves the adhesion, flexibility and water resistance of mortars containing cement, gypsum or lime.
Recommended area of ​​application
Tile adhesive C1: 0.5 - 1.0%
Tile adhesive C2: 2.0 - 5.0%

Product properties
Chemical base VinylAcetate / Acrylic Copolymer (VA / Acrylic Copolymer)
Minimum foaming temperature 5 ± 1 C
Ash content at 600 C 12 ± 2%
Bulk density 400-600 kg / m3
Characteristics
Due to its high adhesion properties, ORP 7099 RD can be used for the production of tile adhesives that are fully compliant with C1 and C2 requirements.
With excellent adhesion, abrasion and water resistance, ORP 7099 RD can be used in repair mortars at a dosage of 1.0 - 2.0%.



ORP 7365 HP
ORP 7365 HP is a redispersible powder obtained by drying a Vinyl Acetate / Acrylic copolymer emulsion with PVA as a protective colloid. The chemical composition of the polymer ensures the coalescence of the redispersible polymer at low temperatures and provides good adhesion to mineral substrates. ORP 7365 HP is used for modifying mixtures containing various binders. Due to its special physical / chemical composition, ORP 7365 HP improves adhesion, abrasion resistance, elasticity and water resistance of mortars.
Recommended area of ​​application
Plastering compounds in SFTK 3.0 - 5.0%
One-component waterproofing mortars 7.0 - 10.0%
Grouting compounds for tiles 2.0 - 4.0%

Product properties
Chemical base VinylAcetate / Acrylic Copolymer (VA / Acrylic Copolymer)
Minimum foaming temperature 0 ± 1 C
Ash content at 600 C 14 ± 2%
Bulk density 400-600 kg / m3
Characteristics
Due to its excellent water resistance, elasticity and compressive strength, ORP 7365 HP can be used for plasters in SPTC.
Due to its excellent flexibility, hydrophobicity and water resistance, ORP 7365 HP can be used in one-component waterproofing mortars.
With excellent abrasion, flexibility and water resistance, ORP 7365 HP can be used in tile grouting compounds.



ORP 7680 SL
ORP 7680 SL is a redispersible powder obtained by drying a Vinyl Acetate / Acrylic copolymer emulsion with PVA as a protective colloid. The specific chemical composition of the polymer ensures the coalescence of the redispersible polymer at low temperatures and ensures good adhesion to various substrates.
ORP 7680 SL is used for modifying mixtures containing various binders. Due to its special physical / chemical composition, ORP 7680 SL improves the adhesion, flexibility and water resistance of mortars containing cement, gypsum or lime. Especially in self-leveling mortars, ORP 7680 SL provides excellent abrasion resistance, high flexural and compressive strength and good leveling during application.
Recommended area of ​​application
Self-leveling compounds with a dosage of 0.5% to 4%
Repair compositions

Product properties
Chemical base VinylAcetate / Acrylic Copolymer (VA / Acrylic Copolymer)
Minimum foaming temperature 5 ± 1 C
Ash content at 600 C 12 ± 2%
Bulk density 400-600 kg / m3
Characteristics
The use of ORP 7680 SL provides high wear resistance, water resistance, flexural and compressive strength.
Reduces sedimentation and efflorescence



ORP Hydroflex 64
ORP Hydroflex 64 is a redispersible powder obtained by drying a Vinyl Acetate / Vinyl Versatate / Acrylic terpolymer emulsion with PVA as a protective colloid. The chemical composition of the polymer ensures the coalescence of the redispersible polymer at low temperatures and ensures good adhesion to mineral substrates. ORP Hydroflex 64 is used for the modification of mixtures containing various binders. Thanks to its special physical / chemical composition, ORP Hydroflex 64 improves the adhesion, elasticity, hydrophobicity and water resistance of mortars. Due to its elasticity, ORP Hydroflex 64 performs very well in transverse deformation conditions.
Recommended area of ​​application
One-component waterproofing mortars 7.0 - 12.0%
Tile adhesives (CG2) at a dosage of 2.0 to 4.0%, no additional hydrophobic agent required
Grouting compounds for tiles 1.5 - 3.0%
Cement-based plasters and topcoats with a dosage of 2.0 - 4.0%

Product properties
Chemical base Vinyl Acetate / Vinyl Versatate / Acrylic Terpolymer VA / VeoVa / Acrylic Terpolymer
Minimum foaming temperature 0 ± 1 C
Ash content at 600 C 12 ± 2%
Bulk density 400-600 kg / m3
Characteristics
ORP Hydroflex 64 can be used in mortar formulations where high flexibility / elasticity, hydrophobicity and water resistance are required at the same time
Excellent performance at low dosages in resilient one-piece membrane formulations



ORP Thermobond 45
ORP Thermobond 45 is a redispersible powder obtained by drying an emulsion of Vinyl Acrylic Copolymer with PVA as a protective colloid. The specific chemical composition of the polymer ensures the coalescence of the redispersible polymer at low temperatures and ensures good adhesion to various substrates. ORP Thermobond 45 is used to modify mixtures containing various binders. Thanks to its special physical / chemical composition, ORP Thermobond 45 improves the adhesion and elasticity of mortars containing cement, gypsum or lime.
Recommended area of ​​application
ORP Thermobond 45 can be used for the production of cement basecoats applied to EPS and XPS boards in SFTC 1.0 - 3.0%.
Adhesives for EPS and XPS boards in SFTK 0.5 - 2.0%.

Product properties
Chemical base Vinyl Acrylic Copolymer
Minimum foaming temperature 5 ± 1 C
Ash content at 600 C 14 ± 2%
Bulk density 400-600 kg / m3
Characteristics
ORP Thermobond 45 can be used in formulations where good flexibility / elasticity, impact resistance and thixotropic mortar behavior are required.



ORP Thermobond 65
ORP Thermobond 65 is a redispersible powder obtained by drying a Vinyl Acetate / VeoVa / Acrylic terpolymer emulsion with PVA as a protective colloid. The chemical composition of the polymer ensures the coalescence of the redispersible polymer at low temperatures and provides good adhesion to mineral substrates. ORP Thermobond 65 is used to modify mixtures containing various binders. Due to its special physical / chemical composition, ORP Thermobond 65 improves the adhesion, elasticity and water resistance of mortars. Especially because of the elastic nature of ORP Thermobond 65 performs well under lateral deformation conditions.
Recommended area of ​​application
Cement basecoats applied to EPS and XPS boards in SFTK 3.0 - 5.0%.
Adhesives for EPS and XPS boards in SFTK 1.0 - 2.0%.
Elastic tile adhesives (S1 and S2) 3.0 - 7.0%.

Product properties
Chemical base Vinyl Acetate / VeoVa / Acrylic Terpolymer (VA / VeoVa / Acrylic Terpolymer)
Minimum foaming temperature 0 C
Ash content at 600 C 12 ± 2%
Bulk density 400-600 kg / m3
Characteristics
ORP Thermobond 65 can be used in formulations where good flexibility / elasticity, impact resistance and thixotropic mortar behavior as well as excellent water resistance are required



ORP Thermobond 74
ORP Thermobond 74 is a redispersible powder obtained by drying a Vinyl Acetate / Acrylic copolymer emulsion with PVA as a protective colloid. The chemical composition of the polymer ensures the coalescence of the redispersible polymer at low temperatures and ensures good adhesion to mineral substrates. ORP Thermobond 74 is used for modifying mixtures containing various binders. Thanks to its special physical / chemical composition, ORP Thermobond 74 improves the adhesion, elasticity and water resistance of mortars. Especially because of the elastic nature of ORP Thermobond 74 works very well under lateral deformation conditions.
Recommended area of ​​application
Cement basecoats applied to EPS and XPS boards in SFTK 3.0 - 5.0%.
Adhesives for EPS and XPS boards in SFTK 1.0 - 2.0%.
Elastic tile adhesives (S1 and S2) 3.0 - 7.0%.

Product properties
Chemical base Vinyl Acetate / Acrylic Copolymer (VA / Acrylic Copolymer)
Minimum foaming temperature 0 C
Ash content at 600 C 14 ± 2%
Bulk density 400-600 kg / m3
Characteristics
ORP Thermobond 74 can be used in formulations where good flexibility / elasticity, impact resistance and thixotropic mortar behavior are required.